摘要：本实验研究了增塑剂对苯二甲酸二辛脂的含量，填充剂的种类和用量，填充剂的表面处理对PVC电缆料性能的影响。通过实验得出结论：增塑剂对苯二甲酸二辛脂能增加PVC的柔韧性和可塑性，但是它也会使PVC的拉伸强度和撕裂强度降低，介电常数增加；填充剂能降低成本，随着填充剂的含量增加会使PVC电缆料的拉伸强度和撕裂强度降低，硬度和密度提高。在碳酸钙、纳米碳酸钙、滑石粉、高岭土这四种填充剂中，滑石粉填充的PVC电缆料力学性能相对较好，高岭土和纳米碳酸钙次之，碳酸钙较差。但是介电常数差别不大；在充油的情况下加入硅烷、铝酸酯、钛酸酯偶联剂表面处理的填充剂会使其力学性能相比之前略微下降，但是介电常数、硬度和密度基本不变。
关键词：对苯二甲酸二辛脂 填充剂 偶联剂 介电常数
Abstract：This experimental study plasticizer DOTP content, the type and amount of filler, filler surface treatment on the performance of the PVC cable. Concluded through experiments can increase the flexibility and plasticity of PVC: plasticizer DOTP, but it will also make PVC, tensile and tear strength decreases, the dielectric constant increase; filler can reduce the cost, with the increase in filler content causes the PVC cable tensile strength and tear strength, hardness and density increased. In the four filler of calcium carbonate, nano calcium carbonate, talc, kaolin, talc-filled PVC cable mechanical properties is relatively good; adding silane in the case of oil-filled aluminum esters, titanate coupling agent surface treatment of fillers will make the mechanical properties for the surface treatment of fillers PVC decreased slightly, but the dielectric constant is essentially the same.
Keywords：DOTP Filler Plasticizer Dielectric constant
增塑剂对苯二甲酸二辛脂能明显的增加PVC的柔韧性和可塑性，但是它也会降低PVC的拉伸强度和撕裂强度，还会使其介电常数增加。在PVC粉体与增塑剂对苯二甲酸二辛脂的比为60：40是其拉伸强度为18.6Mpa，断裂伸长率为270%，撕裂强度为52.9N/mm，硬度为81.9,在频率为1K和1M是介电常数分别为6.1和3.9。
用碳酸钙作为填充剂能降低成本，但是随着碳酸钙含量的增加会使PVC电缆料的拉伸强度和撕裂强度降低，硬度和密度上升，但是介电常数变化不大。
在填充剂碳酸钙、纳米碳酸钙、滑石粉、高岭土中，滑石粉填充的PVC电缆料力学性能相对较好，但是硬度、密度和介电常数差别不大。
在充油的情况下，加入用硅烷、铝酸酯、钛酸酯偶联剂表面处理的填充剂反而会使PVC力学性能略有下降，其中钛酸酯处理的填充剂的力学性能下降幅度较小，但是其硬度、密度和介电常数变化不大。